silicone gel
ZJ-6250H is a high temperature resistant silicon gel, mainly used for
Sealing of IGBT modules and electronic components of optoelectronic equipment
Applied to automotive electronic precision electrical circuits and hybrid circuit modules
Solar cells, sensors, high-power rectifiers, rectifier bridge modules
Product features
Medium viscosity, transparent two-component silicone gel can be cured at room temperature or at high temperature
It has low hardness, low shrinkage, no corrosion, no precipitation of low molecular weight silicone oil, and stable chemical properties
Capable of reliably protecting sensitive microelectronic components from moisture and corrosion
It has better heat resistance than ordinary silicon gel
| Project | Unit | Test method |
Characterization result |
| Before curing | |||
|
Viscosity（mpa.s） |
A |
GB/T 2794 |
450～650 |
|
B |
GB/T 2794 |
900～1100 |
|
|
Density(g/cm3) |
A |
GB/T 13354 |
0.97 |
|
B |
GB/T 13354 |
0.97 |
|
| Mixing ratio |
A:B |
/ |
1:1 |
|
Mixed density(g/cm3) |
A+B |
GB/T 13354 |
0.97 |
|
Operable time/25℃(h) |
A+B |
GB/T 7123 |
2 |
|
Lnitial gel time/25℃(h) |
A+B |
/ |
6 |
|
Curing conditions(℃×min) |
A+B |
/ |
120×30 |
| After curing | |||
|
Density/25℃(g/cm3) |
/ |
0.97 |
|
|
Penetration(2g,mm/10) |
GB 269-85 |
300 |
|
| Dielectric constant |
GB/T1693 |
2.7 |
|
|
Volume resistivity(Ω·cm) |
GB/T 1692 |
1015 |
|
|
Dielectric strength（KV/mm） |
GB/T 1695 |
15 |
|
|
Refractive index/23℃ |
ABBE |
1.405 |
|
|
Transmittance(％) |
UV-VIS |
99 |
|
|
Linear expansion coefficient（ppm） |
/ |
260 |
|
|
Thermal conductivity（W/m.k） |
/ |
0.2 |
|
| Flame retardancy |
UL |
94HB |
|
|
High temperature resistance（220℃×600h） |
/ |
No brittleness or cracking | |
- Before use, thoroughly mix components A and B in a 1:1 ratio. Stir for 5 minutes. It is recommended to use it after 5-10 minutes of vacuuming at -0.09MPa~-0.08MPa
- Temperature and curing time: 25 ℃, starting to thicken after 2.5 hours; Fully cure at 120 ℃ for 30 minutes.
- The mixed adhesive should be sealed, stored, and used up within a safe operating period, otherwise it will slowly solidify and cause waste.
- The curing speed of the adhesive is related to temperature to a certain extent, and curing will be slower at low temperatures.
- This product is not a hazardous material, but do not enter or eye contact. If accidentally splashed, rinse with plenty of water.
- The A and B components of the colloid must be sealed and stored to prevent leakage during transportation!
- Do not contact with N, P, S, plasma compounds such as sulfur, polysulfide, polysulfone or other sulfur containing materials, amine, polyurethane, amide and azide, organotin compounds and silicone rubber containing organotin catalysts to avoid poisoning the platinum catalyst poisoning and curing failure.
A group of 20Kg for component A and 20Kg for component B (small bucket),
Or a set of 180Kg for component A and 180Kg for component B (large barrel)
Store in a dry place for a storage period of 12 months. If it expires, it needs to be retested and can be reused after passing the inspection.
This type of product belongs to non hazardous goods and can be transported as general chemicals.